Lattice stability of Be is estimated,and interaction parameters for the liquids in the Al-Be and Be-Si systems are obtained using phase dia- gram data from literatures.Using the obtained parameters and the lattice stabilities of Al and Si given in the literatures,the Al-Be and Be-Si phase diagrams are calculated.By means of Kohler's for- mula the Gibbs energy for the liquid phase in the Al-Be-Si ternary system is extrapolated.The calcu- lation shows that no excess ternary term is necessa- ry for the thermodynamic description of the system. The liquidus projection,isothermal section at 1273 K,as well as vertical sections at 94 and 88 wt-% Al and 2 wt-% Be are calculated.The calcu- lated results are in reasonable agreement with the experimental data available.
关键词:
thermodynamics
,
null
,
null
,
null
,
null
,
null
SONG Shihong LI Xuzhi ZHANG Weibin Central-South University of Technology
,
Changsha
,
China SONG Shihong
,
Department of materials Science
,
Central-South University of Technology
,
Changsha
,
China
金属学报(英文版)
The correlation between the diverse fracture modes and the microstructural variation with recrystallization in the Al-Li alloys under heat treatment was observed by means of triplanar optical and scanning electron microscopy.The growth,propagation and feature of their frac- tures were described from the viewpoint of microstructure,energy and geometry.